Bone healing around nanocrystalline hydroxyapatite, deproteinized bovine bone mineral, biphasic calcium phosphate, and autogenous bone in mandibular bone defects

Publikation: Bidrag til tidsskriftTidsskriftartikelForskningpeer review

DOI

  1. A method to investigate the biomechanical alterations in Perthes' disease by hip joint contact modeling

    Publikation: Bidrag til tidsskriftTidsskriftartikelForskningpeer review

  2. Examinations of a new long-term degradable electrospun polycaprolactone scaffold in three rat abdominal wall models

    Publikation: Bidrag til tidsskriftTidsskriftartikelForskningpeer review

  1. Implant-supported 2-unit cantilevers compared with single crowns on adjacent implants: A comparative retrospective case series

    Publikation: Bidrag til tidsskriftTidsskriftartikelForskningpeer review

  2. The sandwich osteotomy technique to treat vertical alveolar bone defects prior to implant placement: a systematic review

    Publikation: Bidrag til tidsskriftTidsskriftartikelForskningpeer review

  3. Timing af implantatindsættelse efter traumebetinget tandtab

    Publikation: Bidrag til tidsskriftTidsskriftartikelForskningpeer review

  4. Implant Therapy in the Esthetic Zone

    Publikation: Bidrag til bog/antologi/rapportBidrag til bog/antologiFormidling

  5. Strategies for Treatment of Tooth Loss after Trauma to the Anterior Region of Young Patients

    Publikation: Bidrag til bog/antologi/rapportBidrag til bog/antologiFormidling

  • Nina Broggini
  • Dieter D Bosshardt
  • Simon S Jensen
  • Michael M Bornstein
  • Chun-Cheng Wang
  • Daniel Buser
Vis graf over relationer

The individual healing profile of a given bone substitute with respect to osteogenic potential and substitution rate must be considered when selecting adjunctive grafting materials for bone regeneration procedures. In this study, standardized mandibular defects in minipigs were filled with nanocrystalline hydroxyapatite (HA-SiO), deproteinized bovine bone mineral (DBBM), biphasic calcium phosphate (BCP) with a 60/40% HA/β-TCP (BCP 60/40) ratio, or particulate autogenous bone (A) for histological and histomorphometric analysis. At 2 weeks, percent filler amongst the test groups (DBBM (35.65%), HA-SiO (34.47%), followed by BCP 60/40 (23.64%)) was significantly higher than the more rapidly substituted autogenous bone (17.1%). Autogenous bone yielded significantly more new bone (21.81%) over all test groups (4.91%-7.74%) and significantly more osteoid (5.53%) than BCP 60/40 (3%) and DBBM (2.25%). At 8 weeks, percent filler amongst the test groups (DBBM (31.6%), HA-SiO (31.23%), followed by BCP 60/40 (23.65%)) demonstrated a similar pattern and was again significantly higher as compared to autogenous bone (9.29%). Autogenous bone again exhibited statistically significantly greater new bone (55.13%) over HA-SiO (40.62%), BCP 60/40 (40.21%), and DBBM (36.35%). These results suggest that the osteogenic potential of HA-SiO and BCP is inferior when compared to autogenous bone. However, in instances where a low substitution rate is desired to maintain the volume stability of augmented sites, particularly in the esthetic zone, HA-SiO and DBBM may be favored.

OriginalsprogEngelsk
TidsskriftJournal of Biomedical Materials Research. Part B: Applied Biomaterials
Vol/bind103
Udgave nummer7
Sider (fra-til)1478-87
Antal sider10
ISSN1552-4973
DOI
StatusUdgivet - okt. 2015

ID: 46231277